簡(jiǎn)要描述：SMC不飽合樹(shù)脂層壓板具有較高的機(jī) 械性能和介電性能，較好的耐熱性和耐潮性并有良好的機(jī)械加工性。電機(jī)`電器設(shè)備中作絕緣結(jié)構(gòu)零部件
產(chǎn)品型號(hào)：
所屬分類(lèi)：環(huán)氧樹(shù)脂層壓板
更新時(shí)間：2017-05-06
SMC不飽合樹(shù)脂層壓板
詳細(xì)介紹：
物性表 Properties of Materials
| 品 名 Grade
|
WS-GPO-3 | ||||
適用標(biāo)準(zhǔn) | JIS | TL-GEF | ||||
NEMA | GPO-3 | |||||
材質(zhì) Base and resin
| 不飽合聚脂樹(shù)脂 Unsaturated polyester resin | |||||
試驗(yàn)項(xiàng)目 Testing item | 單位 Unit | 處理?xiàng)l件 Processing Condition | 短切玻璃纖維氈 Chopped stand mad | |||
平行層向耐電壓 Flatwise –with stand voltage | kv/mm | C-90/20/65 | 10 | |||
垂直層向耐電壓 Edgewise-withstand voltage | kv | O-0.5/90 | 10 | |||
絕緣電阻 Insulation resistance
| 常態(tài) Normal condition | MΩ | C-90/20/65
| 105-107 | ||
煮沸后 After boiling | MΩ | C-90/20/65 +D-2/100 | 101-102 | |||
體積電阻系數(shù) Volume resistivity | MΩ-cm | C-90/20/65 | 106-108 | |||
表面電阻系數(shù) Surface resistivity | MΩ | C-90/20/65 | 105-107 | |||
介電常數(shù)(1MHz) Dielectric constant | ― | C-90/20/65 | 4．5-5．0 | |||
介電損耗 (1MHz) Dielectric loss tangent | ― | C- 90/20/65 | 0．020-0．030 | |||
耐電弧性 Arc resistance | sec | A | 180-190 | |||
耐電磨性 Tracking resistance
| V(CTI)
| A | 550-600 | |||
彎曲強(qiáng)度 Flexural strength | 垂直層向 Perpendicular to laminae | MP | A | 180-230 | ||
壓縮強(qiáng)度 Compressive strength
| 垂直層向 Perpendicular to laminae | MPa
| A | 290-390 | ||
平行層向 Parallel to laminae | MPa | A | 150-250 | |||
拉伸強(qiáng)度 Tensile strength
| MPa
| A | 100-200 | |||
楊氏模量 Young’s modulus
| MPa
| A | 12740-15680 | |||
粘結(jié)強(qiáng)度 Bonding strength | kN | A | 5．0-6．5 | |||
洛氏硬度測(cè)量 Rockwell hardness
| HR-R
| A | 115-120 | |||
埃左氏沖擊強(qiáng)度 Izod impact strength | 平行層向 Parallel to laminae | J/cm
| A | 3．4-4．4 | ||
加熱后外觀 Appearance after heating | ℃/2hr | A | 150 | |||
吸水率 (厚 1.0mm) Water absorption(Thickness 1.0mm) | ％ | E -24/50 +D-24/23 | 0．20-0．40 | |||
比重 Specific gravity | ― | A | 1．95-2．05 | |||
熱膨脹系數(shù) Thermal expansion
| 垂直層向 Perpendicular to laminae
| 1/℃ |
RT~ 200℃ | 1．2×10-4 | ||
平行層向 Parallel to laminae | 1/℃ | RT~ 200℃ | 9．6×10-6 | |||
耐燃性 Burning resistance
| UL-94法
| ―
| C-48/23/50 &E-168/70 | UL-94V-0 | ||
鐵路車(chē)輛燃燒試驗(yàn) Burning quality test for rolling stock | ―
| A | 難燃性 | |||